FEP/PFA/ETFE/PVDF Masterbatch and X-ETFE crosslinking

Product category:

Fluoroplastics

Product description:

Our company has invested tens of millions of yuan to introduce several top domestic and foreign silicon steel sheet transverse and longitudinal shear production lines and testing equipment

After nearly ten years of research and development and investment, our company has overcome the difficulties of additive selection, product performance and market application, and the current product quality has reached the international advanced level, mainly engaged in FEP masterbatch, PFA masterbatch, ETFE masterbatch, PVDF masterbatch, various color materials, X-ETFE crosslinking materials and PTFE color paste, can be customized according to customer needs

Key word:

Fluoroplastic:

Transformer core:

Wires:

FEP/PFA/ETFE/PVDF Masterbatch and X-ETFE crosslinking

For FEP and MFA coloring, the color concentrates are made of pure fluoroplastic particles from DuPont, 3M, Daikin, MFA, Juhua, Dongyue, etc., with imported colorants and additives, and produced in strict accordance with advanced technology

For PFA coloring, the color concentrates are made of pure fluoroplastic particles from DuPont, 3M, Daikin, Asahi Glass, MFA, etc., with imported colorants and additives, and produced in strict accordance with advanced technology

For ETFE coloring, the color concentrates are made of pure fluoroplastic particles from DuPont, Daikin, Asahi Glass, etc., with imported colorants and additives, and produced in strict accordance with advanced technology

For PVDF coloring, the color concentrates are made of pure fluoroplastic particles from Arkema, KUREHA, MFA, 3F, etc., with imported colorants and additives, and produced in strict accordance with advanced technology

The cross-links are made of pure fluoroplastic particles from DuPont and Asahi Glass, with imported cross-linking agents and special additives, and produced in strict accordance with advanced technology, for insulation and sheathing of aerospace wires and cables and special cables. It can effectively improve the anti-aging, anti-scratch and anti-puncture capabilities and tensile strength of wire and cable products. In particular, in terms of working temperature, it has been greatly improved, and the maximum working temperature can reach 200℃. In addition, the flame retardant performance of wires and cables has also been improved compared with ordinary ETFE.

It can effectively prevent tiny particles, unevenness and color difference caused by uneven mixing and dispersion of pigment powder, thus ensuring the original performance of fluoroplastics, reducing production costs and optimizing the working environment, improving production efficiency and adapting to automatic production

		Color		RAL Reference color issue
		Black		9011

		Brown		8016

		Red		3020

		Orange		2001

		Yellow		1018

		Green		6032

		Blue		5015

		Purple		4005

		Grey		7012

		White		9016

Weather resistance	1000 hours sunlight ageing test without discolouration
Temperature resistance	No discoloration at 380 degrees for 15 minutes
RoHS	SGS tested and compliant
MFR (Melt index）	FEP：5-35 g/10min ASTM D2116 PFA：5-35 g/10min ASTM D3307 ETFE：5-35 g/10min ASTM D3159 PVDF：5-35 g/10min ASTM D792
specific gravity	FEP：2.15 +/- 0.2 g/cm³ ASTM D792 PFA：2.15 +/- 0.2 g/cm³ ASTM D792 ETFE：1.7 +/- 0.2 g/cm³ ASTM D792 PVDF：1.8 +/- 0.2 g/cm³ ASTM D792
Add a scale (recommended)	3%-10% The final color of the wires varies depending on the color and skin thickness of the conductors.
Color	Refer to the RAL standard number, but also provide user sample color matching services
Particle size	FEP：Ф2.0mm + L2.5mm +/- 0.5 Cylindrical granules PFA：Ф2.0mm + L2.5mm +/- 0.5 Cylindrical granules EFTF：Ф2.0mm + L2.5mm +/- 0.5 Cylindrical granules PVDF：Ф2.5mm + L2.5mm +/- 0.5 Cylindrical granules
Wrap	5kg sealed plastic bag inner packaging plus carton packaging

X-EFTF Technical parameters

melting point	260 C ASTM D-3159
Melt index	14-20 g/10minutes ASTM D-3159
Tensile strength	45 Mpa ASTM D-638
Elongation	>150 % ASTM D-638
Volume resistivity	>10~17 &-cm ASTM D-257
Dielectric constant	2.6 1mHz/23℃ ASTM D-150
Dissipation factor	0.0007 1mHz/23℃ ASTM D-150
specific gravity	1.7 + 0.2 cm³ASTM D-792
Particle size	Ø2.0mm + L2.5mm 士0.5mm Cylindrical granules
Storage conditions	Protect from light at 15-25°C
Wrap	5kg, 10kg, 20kg sealed plastic bag inner packaging plus carton packaging

All of our products are free of substances restricted by RoHS regulations and comply with RoHS requirements. We will have SGS test regularly or have SGS test for each batch according to user requirements

Our company has invested tens of millions of yuan to introduce several top-notch silicon steel sheet transverse and longitudinal shear production lines and testing equipment at home and abroad, producing fixed length silicon steel coils, pre stacked silicon steel sheets, oil immersed transformer lamination cores, energy-saving oil immersed transformer lamination cores, dry type transformer lamination cores, large power transformer lamination cores (including three-phase five columns), special transformer lamination cores, and rectangular reactors. Our company's coil core transformer iron core is made of high-quality silicon steel sheets with low iron loss, which do not require punching and cutting, and there are no punching holes. This eliminates the horizontal and vertical seams of traditional iron cores, reduces magnetic negativity and losses, fully utilizes the orientation of silicon steel, eliminates the increased loss of finished products due to the inconsistent orientation of magnetic circuit and silicon steel, and reduces noise. Compared with S9, the noise is reduced by 7-8dB, the no-load loss is reduced by 30-45%, and the no-load current is reduced by 80%. Using this iron core can manufacture low loss, low noise green and energy-saving transformers, which are highly favored by transformer manufacturers and have a strong market share.

FEP/PFA/ETFE/PVDF Masterbatch and X-ETFE crosslinking